| 245 | 14|aThe synthesis and development of a polymer electrolyte film for use in electrochromic (smart) window technology / |cby K. Such and J. R. Stevens. |
|---|
| 260 | |aOttawa - Ontario : |bNatural Resources Canada. |c1995. |
|---|
| 300 | |a67p. in various pagings. : |bfig., graphs, references, tables ; |c28 cm. |
|---|
| 490 | 1 |a[Technology report] |
|---|
| 500 | |a"The objective of this research was to synthesis polyether/poly(methylmethacrylate)/lithium salt electrolytes as stable elastomeric thin films. Low molecular weight (350g/mol to 600g/mol) polyethers such as poly(ethylene glycol) (PEG) and random copolymers of ethylene oxide (EO)/propylene oxide (PO) blended with poly(methylmethacrylate) (PMMA) or poly(acrylamide) (PMMA) and lithium trifluoromethane sulphonate or lithium triflate (LiCF3SO3) were studied."--Executive summary. |
|---|
| 520 | 3 |aThe objective of this research was to synthesis polyether/poly(methylmethacrylate)/lithium salt electrolytes as stable elastomeric thin films. Low molecular weight (350g/mol to 600g/mol) polyethers such as poly(ethylene glycol) (PEG) and random copolymers of ethylene oxide (EO)/propylene oxide (PO) blended with poly(methylmethacrylate) (PMMA) or poly(acrylamide) (PMMA) and lithium trifluoromethane sulphonate or lithium triflate (LiCF3SO3) were studied.--Executive summary |
|---|
| 546 | |aRésumés en français |
|---|
| 563 | |aRing binding |
|---|
| 690 | 07|aEnergy conservation|2gcpds |
|---|
| 720 | 1 |aSuch, K. |
|---|
| 720 | 1 |aStevens, J. R. |
|---|
| 830 | #0|a[Technology report]|w(CaOODSP)9.514782 |
|---|