| 100 | 1 |aSyrett, B. C. |
|---|
| 245 | 14|aThe effect of pH on the free-corrosion characteristics of 18% Ni (250) maraging steel in 3.5% NaCl solutions |h[electronic resource] / |cB.C. Syrett, Physical Metallurgy Division. |
|---|
| 260 | |aOttawa : |bInformation Canada, |c1970. |
|---|
| 300 | |aiv, 11 p. : |bcharts |
|---|
| 490 | 1 |aTechnical bulletin ; |vTB 126 |
|---|
| 500 | |aCover title. |
|---|
| 500 | |a"July 1970." |
|---|
| 500 | |aDigitized edition from print [produced by Natural Resources Canada]. |
|---|
| 520 | 3 |a“The free-corrosion characteristics of 18% Ni (250) maraging steel in 3.5% NaCl solutions have been studied, using tests in which the ratio of specimen area to solution volume was high (about 0.15 cm2/ml). Initial pH values lay in the range of about 1 to 12, and both aerated and de-aerated solutions were employed. The observations were consistent with the established behaviour of many iron alloys in aqueous media"--Abstract, p. i. |
|---|
| 546 | |aIncludes abstract in French. |
|---|
| 692 | 07|2gccst|aSteel |
|---|
| 710 | 1 |aCanada. |bNatural Resources Canada. |
|---|
| 710 | 1 |aCanada. |bMines Branch. |
|---|
| 830 | #0|aTechnical bulletin (Canada. Dept. of Energy, Mines and Resources. Mines Branch)|vTB 126|w(CaOODSP)9.834857 |
|---|
| 856 | 40|qPDF|s836 KB|uhttps://publications.gc.ca/collections/collection_2017/rncan-nrcan/M34-20/M34-20-126-eng.pdf |
|---|
| 986 | |a300011 |
|---|