| 245 | 10|aPreliminary measurements of the environmental cracking behaviour of titanium alloy 721 |h[electronic resource] / |cG.J. Biefer and J.G. Garrison, Physical Metallurgy Division. |
|---|
| 260 | |aOttawa : |bInformation Canada, |c1971. |
|---|
| 300 | |aiv, 15 p. : |bchart, ill. |
|---|
| 490 | 1 |aTechnical bulletin ; |vTB 132 |
|---|
| 500 | |aCover title. |
|---|
| 500 | |a"February 1971." |
|---|
| 500 | |aDigitized edition from print [produced by Natural Resources Canada]. |
|---|
| 504 | |aIncludes bibliographical references. |
|---|
| 520 | 3 |a“In order to test the functioning of equipment, and to gain some initial experience concerning the environmental cracking susceptibility of Ti-7%Al-2%Nb-1%Ta (Ti-721) alloy, some tests were carried out on notched, precracked specimens loaded as cantilevers. In tests performed in 3.5% NaCl solution, it was confirmed that, subsequent to a sensitizing heat treatment designed to produce Ti3Al (8 hr at 650°C (1202°F)), alloy Ti-721 is extremely susceptible to environmental cracking. It is somewhat more resistant in the as-rolled condition. Environmental cracking tests in which specimens were broken under a gradually rising load were found to give very nearly the same results as did time-to-failure tests under a constant load. It appeared, therefore, that the rising-load method was sufficiently accurate for screening tests of alloys resembling Ti-721, though constant load tests might sometimes be needed for a more precise determination of the critical stress-intensity threshold for cracking, KISCC"--Abstract, p. i. |
|---|
| 546 | |aIncludes abstract in French. |
|---|
| 692 | 07|2gccst|aMetals |
|---|
| 700 | 1 |aGarrison, J. G. |
|---|
| 710 | 1 |aCanada. |bNatural Resources Canada. |
|---|
| 710 | 1 |aCanada. |bMines Branch. |
|---|
| 830 | #0|aTechnical bulletin (Canada. Dept. of Energy, Mines and Resources. Mines Branch)|vTB 132|w(CaOODSP)9.834857 |
|---|
| 856 | 40|qPDF|s2.13 MB|uhttps://publications.gc.ca/collections/collection_2017/rncan-nrcan/M34-20/M34-20-132-eng.pdf |
|---|