| 245 | 10|aComparative corrosion resistance of zinc coatings prepared from Mines Branch and commercial cyanide plating baths |h[electronic resource] / |cA.W. Lui and G.R. Hoey, Extraction Metallurgy Division. |
|---|
| 260 | |aOttawa : |bInformation Canada, |c1973. |
|---|
| 300 | |aiv, 13 p. |
|---|
| 490 | 1 |aTechnical bulletin ; |vTB 166 |
|---|
| 500 | |aCover title. |
|---|
| 500 | |a"February 1973." |
|---|
| 500 | |aDigitized edition from print [produced by Natural Resources Canada]. |
|---|
| 504 | |aIncludes bibliographical references. |
|---|
| 520 | 3 |a“The corrosion resistance of zinc coatings deposited on mild steel from one Mines Branch and three commercial cyanide plating baths were compared by the following three testing methods: (a) neutral salt spray, (b) humidified SO2-air, and (c) combined humidified SO2-air and environmental chamber. No significant difference in corrosion rate was found when coatings of equal thickness prepared from the four different baths were tested under identical conditions. The corrosion resistance of the zinc coatings at various thickness levels indicated that the service lives of the coatings depended on the thickness of zinc applied and not on the type of bath from which the zinc was deposited"--Abstract, p. i. |
|---|
| 546 | |aIncludes abstract in French. |
|---|
| 692 | 07|2gccst|aSteel |
|---|
| 692 | 07|2gccst|aMetals |
|---|
| 700 | 1 |aHoey, G. R. |
|---|
| 710 | 1 |aCanada. |bNatural Resources Canada. |
|---|
| 710 | 1 |aCanada. |bMines Branch. |
|---|
| 830 | #0|aTechnical bulletin (Canada. Dept. of Energy, Mines and Resources. Mines Branch)|vTB 166|w(CaOODSP)9.834857 |
|---|
| 856 | 40|qPDF|s1.01 MB|uhttps://publications.gc.ca/collections/collection_2017/rncan-nrcan/M34-20/M34-20-166-eng.pdf |
|---|