| 245 | 10|aComparison of notch-ductility and weldability of three high-strength structural steels |h[electronic resource] / |cW.P. Campbell. |
|---|
| 260 | |aOttawa : |bCANMET, Energy, Mines and Resources Canada, |c1977. |
|---|
| 300 | |av, 68 p. : |bill. |
|---|
| 490 | 1 |aCANMET report ; |v77-38 |
|---|
| 500 | |aCover title. |
|---|
| 500 | |a"January 1977." |
|---|
| 500 | |a"Minerals Research Program, Physical Metallurgy Research Laboratories." |
|---|
| 500 | |aDigitized edition from print [produced by Natural Resources Canada]. |
|---|
| 504 | |aIncludes bibliographical references (p. 35-36). |
|---|
| 520 | 3 |a"A comparative study was made of the tensile, Charpy V-notch, and drop-weight properties of prime plate and welds in commercially produced T-1 and CET-100 steels and in an experimental Cu-Ni steel which was produced commercially but with further laboratory processing. Comparison was also made of the cold-cracking behaviour of weld heat-affected zones in the three steels and of the behaviour of welds in explosion-bulge tests. Confirmatory crack-starter explosion-bulge tests were made on the Cu-Ni prime plate"--Abstract, p. i. |
|---|
| 546 | |aIncludes abstract in French. |
|---|
| 693 | 4|aSteel, High strength--Ductility |
|---|
| 693 | 4|aSteel, Structural--Ductility |
|---|
| 693 | 4|aSteel, High strength--Weldability |
|---|
| 693 | 4|aSteel, Structural--Weldability |
|---|
| 710 | 1 |aCanada. |bEnergy, Mines and Resources Canada. |
|---|
| 710 | 2 |aCanada Centre for Mineral and Energy Technology. |
|---|
| 710 | 2 |aMinerals Research Program (Canada) |
|---|
| 710 | 2 |aPhysical Metallurgy Research Laboratories (Canada) |
|---|
| 830 | #0|aCANMET report ;|v77-38.|w(CaOODSP)9.852792 |
|---|
| 856 | 40|qPDF|s5.46 MB|uhttps://publications.gc.ca/collections/collection_2019/rncan-nrcan/m38-13/M38-13-77-38-eng.pdf |
|---|