Exploratory stress-corrosion cracking tests on some low-alloy high-strength steels / G.J. Biefer, Physical Metallurgy Division. : M34-20/111E-PDF
“Using a test rig in which the test specimens are small bent strips, held in this configuration under spring loading, stress-corrosion cracking (SCC) tests were performed in several media upon four alloys resembling AISI Type 4320 but with different Si and Mn contents. One of the steels had the composition of “HY-Tuf”, a proprietary steel said to have high resistance to hydrogen embrittlement cracking. A steel containing 1.48% Si and 0.68% Mn showed the best all-round resistance to SCC in tests in normal sulphuric acid (with and without a cathodic "poison"), boiling calcium-ammonium nitrate, and 3.5% NaC1 solution, outperforming the steel having the "HY-Tuf" composition"--Abstract, p. i.
Lien permanent pour cette publication :
publications.gc.ca/pub?id=9.841336&sl=1
| Ministère/Organisme | Canada. Natural Resources Canada. Canada. Mines Branch. |
|---|---|
| Titre | Exploratory stress-corrosion cracking tests on some low-alloy high-strength steels / G.J. Biefer, Physical Metallurgy Division. |
| Titre de la série | Technical bulletin ; TB 111 |
| Type de publication | Série - Voir l'enregistrement principal |
| Langue | [Anglais] |
| Format | Électronique |
| Document électronique | |
| Note(s) | Cover title. "May 1969." Digitized edition from print [produced by Natural Resources Canada]. Includes bibliographical references (p. 7-8). Includes abstract in French. |
| Information sur la publication | Ottawa : Queen's Printer, 1969. |
| Auteur / Contributeur | Biefer, G. J., 1921- |
| Description | ii, 15 p. : ill. |
| Numéro de catalogue |
|
| Numéro de catalogue du ministère | 299997 |
| Descripteurs | Steel |
Demander des formats alternatifs
Pour demander une publication dans un format alternatif, remplissez le formulaire électronique des publications du gouvernement du Canada. Utilisez le champ du formulaire «question ou commentaire» pour spécifier la publication demandée.- Date de modification :