00000nam 2200000za 4500 9.841346 CaOODSP 20221107152050 cr ||||||||||| 170809s1969 oncad ob f000 0 eng d CaOODSP eng eng fre n-cn--- M34-20/114E-PDF M34-20/114 Biefer, G. J., 1921- Stress-corrosion cracking tests on some high-strength steels, using the USNRL cantilever method [electronic resource] / G.J. Biefer and J.G. Garrison, Physical Metallurgy Division. Ottawa : Queen's Printer, 1969. v, 31 p. : charts, ill. Technical bulletin ; TB 114 Cover title. "May 1969." Digitized edition from print [produced by Natural Resources Canada]. Includes bibliographical references. “A stress-corrosion cracking test developed at the U.S. Naval Research Laboratory, Washington, D.C., has been used at the Physical Metallurgy Division to test the cracking susceptibility of a number of high-strength steels. Results are reported which were obtained in stress-corrosion tests on an 18% Ni maraging steel (both parent and weld metal), an HP-9-4-25 steel, a copper-nickel low-alloy steel developed at the Physical Metallurgy Division, and a 17/4 PH stainless steel in each of the H900 and H1000 conditions. For each of these steels, the tendency to fracture under dry conditions was compared with that resulting from immersion in 3.5% NaC1 solution in the unpolarized state. The effects of cathodic protection by 5083 aluminum alloy and zinc were also investigated"--Abstract, p. i. Includes abstract in French. gccst Steel Garrison, J. G. Canada. Natural Resources Canada. Canada. Mines Branch. Technical bulletin (Canada. Dept. of Energy, Mines and Resources. Mines Branch) TB 114 (CaOODSP)9.834857 PDF 4.45 MB https://publications.gc.ca/collections/collection_2017/rncan-nrcan/M34-20/M34-20-114-eng.pdf 300000