24513|aAn evaluation of the microstructure and mechanical properties of submerged-arc and gas-metal-arc welds in HSLA-100 steel / |cby N.J. Smith, J.A. Gianetto, D. Dolan, and J.T. McGrath.
24636|aAn evaluation of the microstructure and mechanical properties of SA and GMA welds in HSLA-100 steel
264 1|aOttawa, ON : |bMetals Technology Laboratories, Canada Centre for Mineral and Energy Technology, |cJuly 1990
300 |a1 online resource (45, [4] pages) : |billustrations, charts
336 |atext|btxt|2rdacontent
337 |acomputer|bc|2rdamedia
338 |aonline resource|bcr|2rdacarrier
4901 |aContractors report ; |v90-28
500 |aCover title.
500 |aDigitized edition from print [produced by Defence Research and Development Canada].
500 |a"This report describes Phase I of a research and development program undertaken by the Fabrication and NDE Section at the Metals Technology Laboratories on behalf of the Defence Research Establishment Pacific under Financial Commitment 89EMR01. DREP Scientific Authority: Dr J. Morrison."--cover page.
504 |aIncludes bibliographical references (page 14).
520 |a"In Phase I of the program the objective was to evaluate commercially-available welding consumables and develop weld procedures for joining HSLA 100 steel using the submerged-arc (SAW) and gas-metal-arc (GMA) welding processes. The evaluation included a quantitative assessment of weld metal microstructure and measurement of weld metal mechanical properties. Phase II of the program will evaluate welding wire formulations that have been designed from the data of Phase I to provide optimum weld metal mechanical properties in the joining of HSLA 100 steel plate. [...] The results obtained in Phase I are given in this report. The Phase I program has two components. Initially, bead-in-groove (BIG) welds were deposited in HSLA 100 plate with a range of commercially-available consumables to provide a fundamental understanding of the effects of weld composition and energy input on the microstructure and resultant mechanical properties of as-deposited weld metal."--introduction (page 1).
650 0|aSteel, High strength|xMechanical properties.
650 0|aSubmerged arc welding|xEvaluation.
650 0|aGas metal arc welding|xEvaluation.
650 6|aAcier à haute résistance|xPropriétés mécaniques.
650 6|aSoudage à l'arc sous flux en poudre|xÉvaluation.
650 6|aSoudage à l'arc sous gaz avec fil plein|xÉvaluation.
655 7|aTechnical reports|2lcgft
655 7|aRapports techniques|2rvmgf
7102 |aMetals Technology Laboratories (Ottawa), |eissuing body.
7102 |aDefence Research Establishment Pacific, |eissuing body.
830#0|aContractors report series ;|v90-28.|w(CaOODSP)9.936079
85640|qPDF|s5.14 MB|uhttps://publications.gc.ca/collections/collection_2024/rddc-drdc/DR52-12-4-1990-eng.pdf